Pure-Stat™
Technologies Inc.
6 mil
anti-static polyethylene film,
Pure-Stat™
meets the electrical requirements of MIL-PRF-81705D, Type II entitled
Barrier Material. Flexible, Electrostatic-Free and Heat Sealable. Humidity
independent and non-corrosive. When tested for Fluoride (F), Chloride (Cl),
Sodium (Na), Sulfate (SO4), Nitrate (NO3), and Phosphate (PO4),
these corrosive contaminants were found to be negligible or immeasurable.
Pure-Stat™
is made from a single layer of non-amine polyethylene. |
|
Properties |
| Color - Clear,
tinted pink, or tinted blue. |
|
| Thickness - 2
mils to 8 mils |
ASTM D 374 |
| Tensile Strength
- 2000 to 3000 PSI |
ASTM D 882 |
| Tearing Strength
- 65 to 450 lbs. per inch |
ASTM D 1004 |
| Elongation (MD%)
- greater than 550 |
ASTM D 882 |
| Dart Impact -
250 to 700 gms |
ASTM D 1709 |
| Burst (Mullen) -
20 to 60 PSI |
ASTM D 774 |
| Surface
Resistivity - <1011 OHMS/Sq. |
ASTM D 257 |
|
|
Performance
|
Static Decay
Rate - 5 KV-0 Volts < 2 seconds per
MIL-PRF-81705D, Type II - Fed. Test Method 101
Method 4046
Polycarbonate Compatibility - 3400 PSI at 73ºF, 2500 PSI at 120ºF, 1700
PSI at 158ºF and 2000 at 185ºF |
|
|
Shelf Life |
Permanently anti-static under normal storage conditions.
Tested:
16 hours @ 0ºF - antistatic
16 hours @ 160ºF - antistatic
8 hours @ 100ºF, 95% RH-antistatic |
|
Sizes |
Bag Width - 1 ¾" to 80"
Bag Length - Any Length Available in reclosable tops.
Minimum 3" |
|
Heat Sealing |
Product is suitable for automatic bag-making machines:
Temperature - 250ºF - 375ºF
Time - 0.5 - 3.5 seconds
Pressure - 30 - 70 PSI |
|
Applications |
For packaging of static sensitive and non-static sensitive components,
where electrostatic contamination is a problem. Products Available - Bags,
Tubing, Sheeting. |
| *The values in the above table were developed from random samples taken from
production material we believe to be typical for the product. Actual
values, however, may vary somewhat from those depicted here and PTI makes no
warranty, expressed or implied, as to the suitability of these materials for any
specific use. Customers should determine product suitability based upon
their own initial criteria. Nothing herein is to be taken as license to
operate under or a recommendation to infringe upon any patent. |